PA66德国巴斯夫8202HS热稳定耐磨损薄壁产品应用

  

   

物性表

物理性能测试条件测试方法测试结果单位收缩率MD：3.18mm
1.2%吸水率24hrASTMD5701.6%23°C,24hrISO621.6%饱和ASTMD5709.5%饱和,23°CISO629.5%平衡,50%RHASTMD5702.7%平衡,23°C,50%RHISO622.7%机械性能测试条件测试方法测试结果单位拉伸模量23°CISO527-22700Mpa80°CISO527-2485Mpa120°CISO527-2360Mpa150°CISO527-2290Mpa抗张强度屈服,-40°CASTMD638126Mpa屈服,23°CASTMD63879.0Mpa屈服,80°CASTMD63835.0MpaYield,121°CASTMD63825.0Mpa拉伸应力屈服,-40°CISO527-2126Mpa屈服,23°CISO527-278.0Mpa屈服,80°CISO527-235.0Mpa弯曲模量23°CASTMD7902830Mpa65°CASTMD790500Mpa90°CASTMD790350Mpa121°CASTMD790305Mpa23°CISO1782400Mpa弯曲强度-40°CASTMD790170Mpa23°CASTMD790108Mpa65°CASTMD79030.0Mpa90°CASTMD79020.0Mpa121°CASTMD79017.0Mpa拉伸应力屈服,120°CISO527-225.0Mpa屈服,150°CISO527-220.0Mpa抗张强度断裂,23°CASTMD63875.0Mpa伸长率屈服,23°CASTMD6384.0%屈服,80°CASTMD63842%Yield,121°CASTMD63836%拉伸应变屈服,23°CISO527-24.0%伸长率断裂,23°CASTMD63855%标称拉伸断裂应变23°CISO527-225%弯曲模量-40°CASTMD7903010Mpa弯曲应力23°CISO17885.0Mpa热性能测试条件测试方法测试结果单位RTIImp1.5mmUL746105°C3.0mmUL746105°C6.0mmUL746105°CRTIStr0.71mmUL74695.0°C1.5mmUL746105°C3.0mmUL746105°C6.0mmUL746105°C热变形温度0.45MPa,未退火ASTMD648178°C0.45MPa,未退火ISO75-2/B150°C1.8MPa,未退火ASTMD64865.0°C1.8MPa,未退火ISO75-2/A60.0°C熔融峰值温度
ASTMD3418220°C溶融温度（DSC）
ISO3146220°C线形热膨胀系数MDASTME8318.3E-05cm/cm/°CRTIElec0.71mmUL746130°C1.5mmUL746130°C3.0mmUL746130°C6.0mmUL746130°CRTIImp0.71mmUL74695.0°C电气性能测试条件测试方法测试结果单位介电强度
IEC60243-137KV/mm漏电起痕指数
IEC60112600VVolumeResistivity1.50mmASTMD257>1.0E+13ohms·cm体积电阻率
IEC60093>1.0E+13ohms·cm介电强度21.50mmASTMD14922KV/mm冲击性能测试条件测试方法测试结果单位简支梁无缺口冲击强度-30°CISO17951kJ/m²23°CISO179NoBreak
落下冲击阻力23°C内部方法142J
-40°CASTMD25648J/m23°CASTMD25658J/m23°CISO1793.5kJ/m²硬度测试条件测试方法测试结果单位洛氏硬度R级ASTMD785119
可燃性测试条件测试方法测试结果单位UL阻燃等级0.71mmUL94V-2
1.5mmUL94V-2
3.0mmUL94V-2
6.0mmUL94V-2